Zeolites Derived from Natural Kaolinite for CO2 Adsorption

This manuscript deals with the synthesis of different types of zeolites from natural kaolinite samples for CO2 adsorption. A zeolite A was prepared from kaolinite by means of an alkaline fusion process, followed by hydrothermal treatment, whereas a highly crystalline zeolite X was synthesized by optimizing the previously mentioned synthetic procedure. In detail, the SiO2/Al2O3 molar ratio in the preliminary mixture was modified with the addition of a secondary silicon source (sodium silicate) in order to obtain the one required for zeolites X. The physicochemical properties of the pristine clay and of the different zeolites were investigated by means of a multi-technique approach, including XRPD; SEM-EDX; Na-23, Al-27 and Si-29 MAS NMR spectroscopy; and N-2 physisorption analysis at 77 K. Since the Si and Al molar ratios and reactivities are key parameters for the synthesis of zeolites, these aspects, primarily related to the use of a naturally occurring aluminosilicate as the raw material, have been investigated for their correlation with the physicochemical properties of the synthetic products. Moreover, by means of a custom-built volumetric apparatus, the CO2 adsorption capacity of the resulting zeolites at low gas pressures (<1 bar) and at 25 degrees C was assessed.