In the present work, a new combination of synthetic and natural biomaterials is proposed for bone tissue engineering (BTE) applications. In order to mimic the inorganic and organic phases of bone extracellular matrix (ECM), a bioactive glass-ceramic deriving from a SiO2–P2O5–CaO–MgO–Na2O–K2O parent glass, acting as a substrate in form of a slice, was surface-functionalised with a type I collagen-based coating. In particular, the collagen was blended with a water soluble polyurethane (PUR), synthesised from poly(ethylene glycol), 1,6-hexamethylene diisocyanate and N-BOC-serinol. The PUR was designed to expose amino groups on the polymeric chain, which can be exploited for the blend stabilisation through crosslinking. The newly synthesised PUR demonstrated to be non-cytotoxic, as assessed by a biological test with MG-63 osteoblast-like cells. The collagen/PUR blend showed good biocompatibility as well. The polymeric coating on the glass-ceramic samples was produced by surface-silanisation, followed by further chemical grafting of the blend, using genipin as a crosslinker. The glass-ceramic surface was characterised at each functionalisation step, demonstrating that the procedure allowed obtaining a covalent link between the blend and the substrate. Finally, biological tests performed using human periosteal derived precursor cells demonstrated that the proposed polymer-coated material was a good substrate for bone cell adhesion and growth, and a good candidate to mimic the composite nature of the bone ECM.
Newly-designed collagen/polyurethane bioartificial blend as coating on bioactive glass-ceramics for bone tissue engineering applications
Cassino, Claudio;
2019-01-01
Abstract
In the present work, a new combination of synthetic and natural biomaterials is proposed for bone tissue engineering (BTE) applications. In order to mimic the inorganic and organic phases of bone extracellular matrix (ECM), a bioactive glass-ceramic deriving from a SiO2–P2O5–CaO–MgO–Na2O–K2O parent glass, acting as a substrate in form of a slice, was surface-functionalised with a type I collagen-based coating. In particular, the collagen was blended with a water soluble polyurethane (PUR), synthesised from poly(ethylene glycol), 1,6-hexamethylene diisocyanate and N-BOC-serinol. The PUR was designed to expose amino groups on the polymeric chain, which can be exploited for the blend stabilisation through crosslinking. The newly synthesised PUR demonstrated to be non-cytotoxic, as assessed by a biological test with MG-63 osteoblast-like cells. The collagen/PUR blend showed good biocompatibility as well. The polymeric coating on the glass-ceramic samples was produced by surface-silanisation, followed by further chemical grafting of the blend, using genipin as a crosslinker. The glass-ceramic surface was characterised at each functionalisation step, demonstrating that the procedure allowed obtaining a covalent link between the blend and the substrate. Finally, biological tests performed using human periosteal derived precursor cells demonstrated that the proposed polymer-coated material was a good substrate for bone cell adhesion and growth, and a good candidate to mimic the composite nature of the bone ECM.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.